Consistent results you can rely on
3D FLASH is engineered for labs that demand both speed and quality.
Its specially engineered powder and advanced manufacturing process ensure stable, consistent performance in both fast and conventional sintering cycles.
Natural Gradient Design
Seamless four-dimensional transitions in color, translucency (57% incisal to 45% cervical), strength (700 MPa incisal to 1100 MPa cervical), and hardness across an 6-layer structure with up to 15 gradient levels.
No Additional Staining Required
Pre-shaded Zirconia Discs enable direct full sintering, eliminating post-processing coloration and ensuring consistent, natural aesthetics.
Superior Durability & Aesthetics
High cervical strength prevents chipping and deformation; enamel-like incisal layer protects opposing teeth.
Rapid sintering
With 40-minute rapid sintering, it significantly reduces production time while maintaining excellent strength and translucency.
Maximum freedom of indication
Inlay/onlay
Veneer
Anterior full crown
Full Contour Posterior Crown
≤6 Unit Bridges
Parameters
| Product Specifications | |||
|---|---|---|---|
| Product name | 3D FLASH Zirconia Blank | Size | 98*10(12/14/16/18/20/22/25/30) mm |
| Processing Service | Milling | OEM | Yes |
| System | 98,95,AG | Color | A1-D4 BL1-4 |
| Flexural Strength | 700-1100 MPa | Translucency | 45%-57% |
| Chemical Composition | |
|---|---|
| ZrO2 + HfO2 + Y2O3 | ≥ 99% |
| Y2O3 | 4.5%-10% |
| Al2O3 | < 0.15% |
| Other Oxides | < 0.5% |